Biomechanical comparison of biodegradable magnesium screws and titanium screws for operative stabilization of displaced capitellar fractures.
Journal of Shoulder and Elbow Surgery 2020 May 14
BACKGROUND: Displaced fractures of the humeral capitellum are commonly treated operatively and fixed by titanium screws (TSs) either directly or indirectly. In the case of direct transcartilaginous fixation, biodegradable screws with the ability to be countersunk can be favorable regarding implant impingement and cartilage destruction. Hence, the goal of this study was to biomechanically compare headless compression screws made from titanium with a biodegradable equivalent made from a magnesium alloy.
METHODS: This biomechanical in vitro study was conducted on 13 pairs of fresh-frozen human cadaveric humeri, in which a standardized Bryan-Morrey type I fracture was fixed using 2 magnesium screws (MSs) or 2 TSs. First, construct stiffness was measured during 10 cycles of static loading between 10 and 50 N. Second, continuous loading was applied at 4 Hz between 10 and 50 N, increasing the maximum load every 10,000 cycles by 25 N until construct failure occurred. This was defined by fragment displacement >3 mm.
RESULTS: Comparison of the 2 screw types showed no differences related to construct stiffness (0.50 ± 0.25 kN/mm in MS group and 0.47 ± 0.13 kN/mm in TS group, P = .701), failure cycle (43,944 ± 21,625 and 41,202 ± 16,457, respectively; P = .701), and load to failure (152 ± 53 N and 150 ± 42 N, respectively; P = .915).
CONCLUSION: Biomechanical comparison showed that simple capitellar fractures are equally stabilized by headless compression screws made from titanium or a biodegradable magnesium alloy. Therefore, in view of the advantages of biodegradable implants for transcartilaginous fracture stabilization, their clinical application should be considered and evaluated.
METHODS: This biomechanical in vitro study was conducted on 13 pairs of fresh-frozen human cadaveric humeri, in which a standardized Bryan-Morrey type I fracture was fixed using 2 magnesium screws (MSs) or 2 TSs. First, construct stiffness was measured during 10 cycles of static loading between 10 and 50 N. Second, continuous loading was applied at 4 Hz between 10 and 50 N, increasing the maximum load every 10,000 cycles by 25 N until construct failure occurred. This was defined by fragment displacement >3 mm.
RESULTS: Comparison of the 2 screw types showed no differences related to construct stiffness (0.50 ± 0.25 kN/mm in MS group and 0.47 ± 0.13 kN/mm in TS group, P = .701), failure cycle (43,944 ± 21,625 and 41,202 ± 16,457, respectively; P = .701), and load to failure (152 ± 53 N and 150 ± 42 N, respectively; P = .915).
CONCLUSION: Biomechanical comparison showed that simple capitellar fractures are equally stabilized by headless compression screws made from titanium or a biodegradable magnesium alloy. Therefore, in view of the advantages of biodegradable implants for transcartilaginous fracture stabilization, their clinical application should be considered and evaluated.
Full text links
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app